Halar® Extended Properties
| General |
|
Comments |
Units |
|
|
| Density |
|
ASTM D792 |
g/cc |
1.68 |
| Melt Flow |
|
1.05kg/190°C |
g/10 min |
2 |
| Water Absorption |
24 hour |
ASTM D570 |
|
0.10 |
| Moisture Absorption at Equillibrium |
50% RH |
ASTM D570 |
% |
<0.01 |
Hardness,
Shore D |
|
ASTM D2240 |
- |
75 |
Hardness,
Rockwell R |
|
ASTM D785 |
- |
90 |
| |
|
|
|
|
| Mechanical |
|
Comments |
Units |
|
|
| Tensile Strength |
Yield |
ASTM D638 |
MPa(psi) |
30(4,300) |
| Tensile Strength |
Break |
ASTM D638 |
MPa(psi) |
54(7,800) |
| Elongation |
Yield |
ASTM D638 |
% |
5 |
| Elongation |
Break |
ASTM D638 |
% |
250 |
| Modulus of Elasticity |
|
ASTM D638 |
GPa(ksi) |
1.6(240) |
| Flexural Modulus |
|
ASTM D790 |
GPa(ksi) |
1.7(245) |
| Flexural Yield Strength |
|
ASTM D790 |
MPa(psi) |
47(6,800) |
| Izod Impact Strength |
|
ASTM D256 |
J/cm |
No break |
| Izod Impact Low Temp |
Notched, at -40°C |
ASTM D256 |
J/m(ftlb/in) |
207(2.0) |
| Coefficient of Friction |
Dynamic vs. carbon steel, 50mm/s (2in/s) |
ASTM D1894 |
|
0.2 |
| |
|
|
|
|
| Thermal |
|
Comments |
Units |
|
|
| Coefficient of Thermal Expansion |
linear 20°C |
|
µin/in-°F |
56 |
| Deflection Temperature |
at 1.8 MPa |
ASTM D648 |
°C(°F) |
63(145) |
| Melting Point °C |
|
ASTM D3418 |
°C(°F) |
240(464) |
| Maximum Service Temperature |
Deflection Temp at 1.8 MPa |
- |
°C(°F) |
148(300) |
| Thermal Conductivity |
|
- |
(W/m-K)BTU-in/hr-ft2-°F |
1.05(1.09) |
| Flammability |
UL-94 @3.1 mm |
UL94 |
Class |
V-0 |
| |
|
|
|
|
| Electrical |
|
Comments |
Units |
|
|
| Electrical Resestivity |
|
ASTM D257 |
Ohm-cm |
5.5E+16 |
| Dielectric Constant |
at 1MHz |
ASTM D150 |
- |
2.57 |
| Dielectric Strength, kV/mm |
3.2mm (90 mils); Short Time |
ASTM D149 |
Volts/mil(kV/mm) |
350(14) |
| Dissipation Factor |
at 1 MHz |
ASTM D150 |
- |
0.013 |
| Arc Resistance |
|
ASTM D495 |
sec |
50 |