| General |
|
Method |
Units |
|
|
| Water Absorption |
24 hr. |
D570 |
% |
<0.03 |
| Weather and Chemical Resistance |
|
- |
- |
Outstanding |
| Limiting Oxygen Index |
|
D2863 |
% |
>93 |
| |
|
|
|
|
| Mechanical |
|
Method |
Units |
|
|
| Tensile Strength |
23°C (73°F)
250°C (482°F)
23°C (73°F)(yield) |
D3307
D3307
D3307 |
MPa(psi)
MPa(psi)
MPa(psi) |
25(3,600)
14(1,800)
13.8(2,000) |
| Ultimate Elongation |
23°C (73°F)
250°C (482°F) |
D790
D790 |
%
% |
300
480 |
| Flexural Modulus |
23°C (73°F)
250°C (482°F) |
D3307
D3307 |
MPa(psi)
MPa(psi) |
590(85,000)
55(8,000) |
| Specific Gravity |
|
D792 |
- |
2.12-2.17 |
| Hardness Durometer |
|
D2240 |
- |
D55 |
| MIT Folding Endurance |
0.18-0.20mm(.007-.008 in.) |
D2176 |
Cycles |
15,000 |
| |
|
|
|
|
| Thermal |
|
Method |
Units |
|
|
| Nominal Melting Point |
|
DTA-E168 |
°C (°F) |
302-310 (575-590) |
| Coefficient of Thermal Expansion |
21-100°C
70-212°F
100-149°C
212-300°F
149-208°C
300-408°F |
D696
D696
D696
D696
D696
D696 |
mm/mm/°C
in./in./°F
mm/mm/°C
in./in./°F
mm/mm/°C
in./in./°F |
14x10-5
7.6x10-5
17x10-5
9.2x10-5
21x10-5
11.5x10-5 |
| Upper Service Temperature |
|
- |
°C (°F) |
260(500) |
| Flow Rate |
|
D3307
D3307
D3307 |
g/10 min
g/10 min
g/10 min |
12-15(B)
15-18(A)
18-21(D) |
| |
|
|
|
|
| Electrical |
|
Method |
Units |
|
|
| Dielectric Strength |
Short time, 0.25 mm (0.10 in) |
D149 |
kV/mm (V/mil) |
80(2,000) |
| Dielectric Constant |
60 - 106 Hz |
D150 |
- |
2.03 |
| Dissipation Factor |
60 - 106 Hz |
D150 |
- |
0.0001 |
| Volume Resistivity |
|
D-257 |
ohm-cm |
1018 |